Wironit® 1000 g

• Successful worldwide since 1953 – ideally suited for conventional clasp partial dentures

• The reduced Vickers hardness allows easier finishing and polishing

• The clasps can be activated very easily by the dentist

• Biocompatible and corrosion-resistant

• Item name

  Wironit®
• Casting temperature

  1460 °C
• Vickershardness

  360 HV10
• Product description

  Cobalt-Chromium partial denture alloy
• Liquidustemp.

  1395 °C
• Solidustemp

  1265 °C
• Preheat temp. to

  1050 °C
• Preheat temp. from

  950 °C
• Density g/cm³

  8,3 g/cm³
• Composition

  Co 64,0 · Cr 28,5 · Mo 5,0 · Si 1,0 · Mn 1,0 · C
• Iso type ISO22674

  5
• Color code

  8
• Base metall

  Cobalt
• Content/amount

  1000 g pack
• Yield strength

  615 MPa
• Tensile strength

  895 MPa
• Elongation at break

  10 %
• Elastic modul

  185 GPa