Wirobond® C 1000 g

• Nickel- and beryllium-free

• Simple processing thanks to reliable casting time recognition

• Carbon-free composition – particularly well suited for laser welding

• The element cerium ensures high bond strength with the ceramic, minimising the risk of subsequent flaking or chipping

• Low thermal conductivity – protects the pulp and ensures high wearing comfort for the patient

• Biocompatible and corrosion-resistant thanks to a firmly-adhering passive layer

• Item name

  Wirobond® C
• Iso type ISO22674

  5
• Density g/cm³

  8,5 g/cm³
• Preheat temp. to

  1000 °C
• Liquidustemp.

  1420 °C
• CTE

  14,3 10ˉ⁶ Kˉ¹
• Product description

  Cobalt-Chromium alloy for crowns & bridges
• Vickershardness

  315 HV10
• Casting temperature

  1500 °C
• Composition

  Co 63,3 · Cr 24,8 · W 5,3 · Mo 5,1 · Si 1,0 · Ce
• Preheat temp. from

  900 °C
• Color code

  8
• Base metall

  Cobalt
• Content/amount

  1000 g pack
• Yield strength

  440 MPa
• Tensile strength

  780 MPa
• Elongation at break

  16 %
• Solidustemp

  1360 °C
• Elastic modul

  180 GPa